AWS E320LR vs. EN 1.5410 Steel
Both AWS E320LR and EN 1.5410 steel are iron alloys. They have a modest 40% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS E320LR and the bottom bar is EN 1.5410 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 34 | |
| 20 to 25 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 560 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1460 |
| Melting Onset (Solidus), °C | 1360 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 2.3 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 6.2 | |
| 1.7 |
| Embodied Energy, MJ/kg | 87 | |
| 22 |
| Embodied Water, L/kg | 220 | |
| 49 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 20 to 22 |
| Strength to Weight: Bending, points | 19 | |
| 19 to 21 |
| Thermal Shock Resistance, points | 15 | |
| 16 to 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.12 |
| Chromium (Cr), % | 19 to 21 | |
| 0 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 |
| Iron (Fe), % | 32.7 to 42.5 | |
| 96.9 to 98.6 |
| Manganese (Mn), % | 1.5 to 2.5 | |
| 1.2 to 1.8 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0.2 to 0.4 |
| Nickel (Ni), % | 32 to 36 | |
| 0 |
| Niobium (Nb), % | 0 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.1 |