AWS E320LR vs. Nickel 600

AWS E320LR belongs to the iron alloys classification, while nickel 600 belongs to the nickel alloys. They have 58% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E320LR and the bottom bar is nickel 600.

AWS E320LR (W88022) Weld Metal Nickel Alloy 600 (N06600, NA14)

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		34
Elongation at Break, %		3.4 to 35

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		77
Shear Modulus, GPa		75

Tensile Strength: Ultimate (UTS), MPa		580
Tensile Strength: Ultimate (UTS), MPa		650 to 990

Thermal Properties

Latent Heat of Fusion, J/g		300
Latent Heat of Fusion, J/g		310

Melting Completion (Liquidus), °C		1410
Melting Completion (Liquidus), °C		1410

Melting Onset (Solidus), °C		1360
Melting Onset (Solidus), °C		1350

Specific Heat Capacity, J/kg-K		460
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		36
Base Metal Price, % relative		55

Density, g/cm³		8.2
Density, g/cm³		8.5

Embodied Carbon, kg CO₂/kg material		6.2
Embodied Carbon, kg CO₂/kg material		9.0

Embodied Energy, MJ/kg		87
Embodied Energy, MJ/kg		130

Embodied Water, L/kg		220
Embodied Water, L/kg		250

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		20
Strength to Weight: Axial, points		21 to 32

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		20 to 26

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		19 to 29

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0 to 0.15

Chromium (Cr), %		19 to 21
Chromium (Cr), %		14 to 17

Copper (Cu), %		3.0 to 4.0
Copper (Cu), %		0 to 0.5

Iron (Fe), %		32.7 to 42.5
Iron (Fe), %		6.0 to 10

Manganese (Mn), %		1.5 to 2.5
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		2.0 to 3.0
Molybdenum (Mo), %		0

Nickel (Ni), %		32 to 36
Nickel (Ni), %		72 to 80

Niobium (Nb), %		0 to 0.4
Niobium (Nb), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.3
Silicon (Si), %		0 to 0.5

Sulfur (S), %		0 to 0.015
Sulfur (S), %		0 to 0.015