AWS E33-31 vs. EN 1.8151 Steel

Both AWS E33-31 and EN 1.8151 steel are iron alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E33-31 and the bottom bar is EN 1.8151 steel.

AWS E33-31 (W33310) Weld Metal EN 1.8151 (45SiCrV6-2) Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.27
Poisson's Ratio		0.29

Shear Modulus, GPa		81
Shear Modulus, GPa		72

Tensile Strength: Ultimate (UTS), MPa		810
Tensile Strength: Ultimate (UTS), MPa		670 to 1940

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		270

Melting Completion (Liquidus), °C		1380
Melting Completion (Liquidus), °C		1440

Melting Onset (Solidus), °C		1330
Melting Onset (Solidus), °C		1400

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		13

Otherwise Unclassified Properties

Base Metal Price, % relative		36
Base Metal Price, % relative		2.2

Density, g/cm³		7.9
Density, g/cm³		7.7

Embodied Carbon, kg CO₂/kg material		6.0
Embodied Carbon, kg CO₂/kg material		1.8

Embodied Energy, MJ/kg		86
Embodied Energy, MJ/kg		25

Embodied Water, L/kg		260
Embodied Water, L/kg		49

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		28
Strength to Weight: Axial, points		24 to 70

Strength to Weight: Bending, points		24
Strength to Weight: Bending, points		22 to 45

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		20 to 58

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0.4 to 0.5

Chromium (Cr), %		31 to 35
Chromium (Cr), %		0.4 to 0.8

Copper (Cu), %		0.4 to 0.8
Copper (Cu), %		0

Iron (Fe), %		24.7 to 34.8
Iron (Fe), %		95.9 to 97.2

Manganese (Mn), %		2.5 to 4.0
Manganese (Mn), %		0.6 to 0.9

Molybdenum (Mo), %		1.0 to 2.0
Molybdenum (Mo), %		0

Nickel (Ni), %		30 to 32
Nickel (Ni), %		0

Nitrogen (N), %		0.3 to 0.5
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.025

Silicon (Si), %		0 to 0.9
Silicon (Si), %		1.3 to 1.7

Sulfur (S), %		0 to 0.010
Sulfur (S), %		0 to 0.025

Vanadium (V), %		0
Vanadium (V), %		0.1 to 0.2