AWS E33-31 vs. EN 1.8880 Steel

Both AWS E33-31 and EN 1.8880 steel are iron alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E33-31 and the bottom bar is EN 1.8880 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 29
16
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 810
830

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1330
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 36
3.7
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 6.0
1.9
Embodied Energy, MJ/kg 86
26
Embodied Water, L/kg 260
54

Common Calculations

PREN (Pitting Resistance) 44
2.0
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28
29
Strength to Weight: Bending, points 24
25
Thermal Shock Resistance, points 19
24

Alloy Composition

Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 31 to 35
0 to 1.5
Copper (Cu), % 0.4 to 0.8
0 to 0.3
Iron (Fe), % 24.7 to 34.8
91.9 to 100
Manganese (Mn), % 2.5 to 4.0
0 to 1.7
Molybdenum (Mo), % 1.0 to 2.0
0 to 0.7
Nickel (Ni), % 30 to 32
0 to 2.5
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0.3 to 0.5
0 to 0.015
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.9
0 to 0.8
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.12
Zirconium (Zr), % 0
0 to 0.15