AWS E33-31 vs. QE22A Magnesium
AWS E33-31 belongs to the iron alloys classification, while QE22A magnesium belongs to the magnesium alloys. There are 18 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AWS E33-31 and the bottom bar is QE22A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 44 |
| Elongation at Break, % | 29 | |
| 2.4 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 81 | |
| 17 |
| Tensile Strength: Ultimate (UTS), MPa | 810 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 340 |
| Melting Completion (Liquidus), °C | 1380 | |
| 640 |
| Melting Onset (Solidus), °C | 1330 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 970 |
| Thermal Expansion, µm/m-K | 14 | |
| 27 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 2.0 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 27 |
| Embodied Energy, MJ/kg | 86 | |
| 220 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 60 |
| Strength to Weight: Axial, points | 28 | |
| 36 |
| Strength to Weight: Bending, points | 24 | |
| 46 |
| Thermal Shock Resistance, points | 19 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 31 to 35 | |
| 0 |
| Copper (Cu), % | 0.4 to 0.8 | |
| 0 to 0.1 |
| Iron (Fe), % | 24.7 to 34.8 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 93.1 to 95.8 |
| Manganese (Mn), % | 2.5 to 4.0 | |
| 0 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 30 to 32 | |
| 0 to 0.010 |
| Nitrogen (N), % | 0.3 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.9 | |
| 0 |
| Silver (Ag), % | 0 | |
| 2.0 to 3.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Unspecified Rare Earths, % | 0 | |
| 1.8 to 2.5 |
| Zirconium (Zr), % | 0 | |
| 0.4 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |