AWS E330H vs. EN 1.0590 Steel

Both AWS E330H and EN 1.0590 steel are iron alloys. They have 48% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E330H and the bottom bar is EN 1.0590 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11
19
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 690
620

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 30
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.6
Embodied Energy, MJ/kg 76
22
Embodied Water, L/kg 180
48

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 19
20

Alloy Composition

Carbon (C), % 0.35 to 0.45
0 to 0.24
Chromium (Cr), % 14 to 17
0
Copper (Cu), % 0 to 0.75
0 to 0.6
Iron (Fe), % 40.5 to 51.7
96.4 to 100
Manganese (Mn), % 1.0 to 2.5
0 to 1.8
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 33 to 37
0
Niobium (Nb), % 0
0 to 0.060
Nitrogen (N), % 0
0 to 0.027
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.040
Titanium (Ti), % 0
0 to 0.060
Vanadium (V), % 0
0 to 0.15