AWS E330H vs. EN 1.4031 Stainless Steel

Both AWS E330H and EN 1.4031 stainless steel are iron alloys. They have 61% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E330H and the bottom bar is EN 1.4031 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11
11 to 13
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 690
670 to 900

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1350
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
30
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
3.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.7

Otherwise Unclassified Properties

Base Metal Price, % relative 30
7.0
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 5.4
1.9
Embodied Energy, MJ/kg 76
27
Embodied Water, L/kg 180
100

Common Calculations

PREN (Pitting Resistance) 17
14
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
24 to 32
Strength to Weight: Bending, points 22
22 to 27
Thermal Diffusivity, mm2/s 3.2
8.1
Thermal Shock Resistance, points 19
23 to 32

Alloy Composition

Carbon (C), % 0.35 to 0.45
0.36 to 0.42
Chromium (Cr), % 14 to 17
12.5 to 14.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 40.5 to 51.7
83 to 87.1
Manganese (Mn), % 1.0 to 2.5
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 33 to 37
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015