AWS E330H vs. SAE-AISI H24 Steel
Both AWS E330H and SAE-AISI H24 steel are iron alloys. They have 50% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AWS E330H and the bottom bar is SAE-AISI H24 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 720 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 240 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1750 |
| Melting Onset (Solidus), °C | 1350 | |
| 1700 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 420 |
| Thermal Conductivity, W/m-K | 12 | |
| 27 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 37 |
| Density, g/cm3 | 8.1 | |
| 9.1 |
| Embodied Carbon, kg CO2/kg material | 5.4 | |
| 6.1 |
| Embodied Energy, MJ/kg | 76 | |
| 93 |
| Embodied Water, L/kg | 180 | |
| 78 |
Common Calculations
| PREN (Pitting Resistance) | 17 | |
| 28 |
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 24 | |
| 22 to 61 |
| Strength to Weight: Bending, points | 22 | |
| 20 to 39 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 6.9 |
| Thermal Shock Resistance, points | 19 | |
| 22 to 61 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.45 | |
| 0.42 to 0.53 |
| Chromium (Cr), % | 14 to 17 | |
| 2.5 to 3.5 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 to 0.25 |
| Iron (Fe), % | 40.5 to 51.7 | |
| 78 to 82.4 |
| Manganese (Mn), % | 1.0 to 2.5 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 33 to 37 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.15 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 14 to 16 |
| Vanadium (V), % | 0 | |
| 0.4 to 0.6 |