AWS E330H vs. C96900 Copper-nickel
AWS E330H belongs to the iron alloys classification, while C96900 copper-nickel belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AWS E330H and the bottom bar is C96900 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 11 | |
| 4.5 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 210 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1060 |
| Melting Onset (Solidus), °C | 1350 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
| 9.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
| 9.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 39 |
| Density, g/cm3 | 8.1 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 5.4 | |
| 4.6 |
| Embodied Energy, MJ/kg | 76 | |
| 72 |
| Embodied Water, L/kg | 180 | |
| 360 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 24 | |
| 27 |
| Strength to Weight: Bending, points | 22 | |
| 23 |
| Thermal Shock Resistance, points | 19 | |
| 30 |
Alloy Composition
| Carbon (C), % | 0.35 to 0.45 | |
| 0 |
| Chromium (Cr), % | 14 to 17 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 73.6 to 78 |
| Iron (Fe), % | 40.5 to 51.7 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.15 |
| Manganese (Mn), % | 1.0 to 2.5 | |
| 0.050 to 0.3 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 33 to 37 | |
| 14.5 to 15.5 |
| Niobium (Nb), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 7.5 to 8.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |