AWS E347 vs. C11300 Copper
AWS E347 belongs to the iron alloys classification, while C11300 copper belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS E347 and the bottom bar is C11300 copper.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
120 |
Elongation at Break, % | 34 | |
2.3 to 50 |
Poisson's Ratio | 0.28 | |
0.34 |
Shear Modulus, GPa | 77 | |
43 |
Tensile Strength: Ultimate (UTS), MPa | 580 | |
230 to 410 |
Thermal Properties
Latent Heat of Fusion, J/g | 290 | |
210 |
Melting Completion (Liquidus), °C | 1430 | |
1080 |
Melting Onset (Solidus), °C | 1380 | |
1030 |
Specific Heat Capacity, J/kg-K | 480 | |
390 |
Thermal Conductivity, W/m-K | 16 | |
390 |
Thermal Expansion, µm/m-K | 14 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
100 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
100 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 19 | |
32 |
Density, g/cm3 | 7.8 | |
9.0 |
Embodied Carbon, kg CO2/kg material | 3.7 | |
2.6 |
Embodied Energy, MJ/kg | 53 | |
42 |
Embodied Water, L/kg | 150 | |
340 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
7.2 |
Stiffness to Weight: Bending, points | 25 | |
18 |
Strength to Weight: Axial, points | 21 | |
7.2 to 13 |
Strength to Weight: Bending, points | 20 | |
9.4 to 14 |
Thermal Diffusivity, mm2/s | 4.2 | |
110 |
Thermal Shock Resistance, points | 15 | |
8.2 to 15 |
Alloy Composition
Carbon (C), % | 0 to 0.080 | |
0 |
Chromium (Cr), % | 18 to 21 | |
0 |
Copper (Cu), % | 0 to 0.75 | |
99.85 to 99.973 |
Iron (Fe), % | 61.9 to 72.5 | |
0 |
Manganese (Mn), % | 0.5 to 2.5 | |
0 |
Molybdenum (Mo), % | 0 to 0.75 | |
0 |
Nickel (Ni), % | 9.0 to 11 | |
0 |
Niobium (Nb), % | 0 to 1.0 | |
0 |
Phosphorus (P), % | 0 to 0.040 | |
0 |
Silicon (Si), % | 0 to 1.0 | |
0 |
Silver (Ag), % | 0 | |
0.027 to 0.050 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Residuals, % | 0 | |
0 to 0.1 |