AWS E347 vs. C52100 Bronze

AWS E347 belongs to the iron alloys classification, while C52100 bronze belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E347 and the bottom bar is C52100 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
41
Tensile Strength: Ultimate (UTS), MPa 580
380 to 800

Thermal Properties

Latent Heat of Fusion, J/g 290
200
Melting Completion (Liquidus), °C 1430
1030
Melting Onset (Solidus), °C 1380
880
Specific Heat Capacity, J/kg-K 480
370
Thermal Conductivity, W/m-K 16
62
Thermal Expansion, µm/m-K 14
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
13
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
13

Otherwise Unclassified Properties

Base Metal Price, % relative 19
34
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 3.7
3.4
Embodied Energy, MJ/kg 53
55
Embodied Water, L/kg 150
370

Common Calculations

Stiffness to Weight: Axial, points 14
7.0
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21
12 to 25
Strength to Weight: Bending, points 20
13 to 22
Thermal Diffusivity, mm2/s 4.2
19
Thermal Shock Resistance, points 15
14 to 28

Alloy Composition

Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 18 to 21
0
Copper (Cu), % 0 to 0.75
89.8 to 93
Iron (Fe), % 61.9 to 72.5
0 to 0.1
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0.5 to 2.5
0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 9.0 to 11
0
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0.030 to 0.35
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
7.0 to 9.0
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0
0 to 0.5