AWS E349 vs. S35000 Stainless Steel

Both AWS E349 and S35000 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E349 and the bottom bar is S35000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 29
2.3 to 14
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
78
Tensile Strength: Ultimate (UTS), MPa 770
1300 to 1570

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 14
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 25
14
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.9
3.2
Embodied Energy, MJ/kg 72
44
Embodied Water, L/kg 150
130

Common Calculations

PREN (Pitting Resistance) 24
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 27
46 to 56
Strength to Weight: Bending, points 24
34 to 38
Thermal Diffusivity, mm2/s 4.1
4.4
Thermal Shock Resistance, points 20
42 to 51

Alloy Composition

Carbon (C), % 0 to 0.13
0.070 to 0.11
Chromium (Cr), % 18 to 21
16 to 17
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 60.5 to 71.1
72.7 to 76.9
Manganese (Mn), % 0.5 to 2.5
0.5 to 1.3
Molybdenum (Mo), % 0.35 to 0.65
2.5 to 3.2
Nickel (Ni), % 8.0 to 10
4.0 to 5.0
Niobium (Nb), % 0.75 to 1.2
0
Nitrogen (N), % 0
0.070 to 0.13
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0 to 0.15
0
Tungsten (W), % 1.3 to 1.8
0
Vanadium (V), % 0.1 to 0.3
0