MakeItFrom.com
Menu (ESC)

AWS E409Nb vs. EN 1.0487 Steel

Both AWS E409Nb and EN 1.0487 steel are iron alloys. They have 86% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E409Nb and the bottom bar is EN 1.0487 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
27
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 500
440
Tensile Strength: Yield (Proof), MPa 380
280

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
49
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 13
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.9
1.5
Embodied Energy, MJ/kg 42
20
Embodied Water, L/kg 100
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
100
Resilience: Unit (Modulus of Resilience), kJ/m3 380
200
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 6.8
13
Thermal Shock Resistance, points 14
14

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.12
0 to 0.16
Chromium (Cr), % 11 to 14
0 to 0.3
Copper (Cu), % 0 to 0.75
0 to 0.3
Iron (Fe), % 80.2 to 88.5
96.6 to 99.38
Manganese (Mn), % 0 to 1.0
0.6 to 1.5
Molybdenum (Mo), % 0 to 0.75
0 to 0.080
Nickel (Ni), % 0 to 0.6
0 to 0.5
Niobium (Nb), % 0.5 to 1.5
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.050