AWS E409Nb vs. C68000 Brass
AWS E409Nb belongs to the iron alloys classification, while C68000 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS E409Nb and the bottom bar is C68000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 23 | |
| 27 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 76 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 380 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 880 |
| Melting Onset (Solidus), °C | 1410 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 25 | |
| 96 |
| Thermal Expansion, µm/m-K | 14 | |
| 21 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 23 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 42 | |
| 48 |
| Embodied Water, L/kg | 100 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 82 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 | |
| 95 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 18 | |
| 14 |
| Strength to Weight: Bending, points | 18 | |
| 15 |
| Thermal Diffusivity, mm2/s | 6.8 | |
| 31 |
| Thermal Shock Resistance, points | 14 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Carbon (C), % | 0 to 0.12 | |
| 0 |
| Chromium (Cr), % | 11 to 14 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 56 to 60 |
| Iron (Fe), % | 80.2 to 88.5 | |
| 0.25 to 1.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.010 to 0.5 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 0 to 0.6 | |
| 0.2 to 0.8 |
| Niobium (Nb), % | 0.5 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.040 to 0.15 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.75 to 1.1 |
| Zinc (Zn), % | 0 | |
| 35.6 to 42.8 |
| Residuals, % | 0 | |
| 0 to 0.5 |