AWS E409Nb vs. C75400 Nickel Silver
AWS E409Nb belongs to the iron alloys classification, while C75400 nickel silver belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS E409Nb and the bottom bar is C75400 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 23 | |
| 2.0 to 43 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 76 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 370 to 630 |
| Tensile Strength: Yield (Proof), MPa | 380 | |
| 130 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1080 |
| Melting Onset (Solidus), °C | 1410 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Conductivity, W/m-K | 25 | |
| 36 |
| Thermal Expansion, µm/m-K | 14 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.9 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.3 | |
| 7.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 32 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.8 |
| Embodied Energy, MJ/kg | 42 | |
| 59 |
| Embodied Water, L/kg | 100 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 12 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 | |
| 75 to 1450 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.9 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 18 | |
| 12 to 21 |
| Strength to Weight: Bending, points | 18 | |
| 13 to 19 |
| Thermal Diffusivity, mm2/s | 6.8 | |
| 11 |
| Thermal Shock Resistance, points | 14 | |
| 12 to 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.12 | |
| 0 |
| Chromium (Cr), % | 11 to 14 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 63.5 to 66.5 |
| Iron (Fe), % | 80.2 to 88.5 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 0 to 0.6 | |
| 14 to 16 |
| Niobium (Nb), % | 0.5 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 16.2 to 22.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |