MakeItFrom.com
Menu (ESC)

AWS E410 vs. EN 1.4125 Stainless Steel

Both AWS E410 and EN 1.4125 stainless steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E410 and the bottom bar is EN 1.4125 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
19
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 580
800
Tensile Strength: Yield (Proof), MPa 440
470

Thermal Properties

Latent Heat of Fusion, J/g 270
280
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 28
15
Thermal Expansion, µm/m-K 14
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.0
2.3
Embodied Energy, MJ/kg 28
32
Embodied Water, L/kg 100
120

Common Calculations

PREN (Pitting Resistance) 13
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
130
Resilience: Unit (Modulus of Resilience), kJ/m3 500
570
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
29
Strength to Weight: Bending, points 20
25
Thermal Diffusivity, mm2/s 7.5
4.1
Thermal Shock Resistance, points 16
29

Alloy Composition

Carbon (C), % 0 to 0.12
1.0 to 1.2
Chromium (Cr), % 11 to 13.5
16 to 18
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 82.2 to 89
78 to 82.7
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
0.4 to 0.8
Nickel (Ni), % 0 to 0.7
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015