AWS E410 vs. CR007A Copper

AWS E410 belongs to the iron alloys classification, while CR007A copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS E410 and the bottom bar is CR007A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 23
15
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
43
Tensile Strength: Ultimate (UTS), MPa 580
230
Tensile Strength: Yield (Proof), MPa 440
140

Thermal Properties

Latent Heat of Fusion, J/g 270
210
Melting Completion (Liquidus), °C 1450
1090
Melting Onset (Solidus), °C 1400
1040
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 28
380
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
100
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
100

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
31
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 2.0
2.6
Embodied Energy, MJ/kg 28
41
Embodied Water, L/kg 100
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
31
Resilience: Unit (Modulus of Resilience), kJ/m3 500
83
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21
7.1
Strength to Weight: Bending, points 20
9.3
Thermal Diffusivity, mm2/s 7.5
110
Thermal Shock Resistance, points 16
8.1

Alloy Composition

Antimony (Sb), % 0
0 to 0.00040
Arsenic (As), % 0
0 to 0.00050
Bismuth (Bi), % 0
0 to 0.00020
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 11 to 13.5
0
Copper (Cu), % 0 to 0.75
99.994 to 100
Iron (Fe), % 82.2 to 89
0 to 0.0010
Lead (Pb), % 0
0 to 0.00050
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 0 to 0.7
0
Phosphorus (P), % 0 to 0.040
0
Selenium (Se), % 0
0 to 0.00020
Silicon (Si), % 0 to 0.9
0
Silver (Ag), % 0
0 to 0.0025
Sulfur (S), % 0 to 0.030
0 to 0.0015
Tellurium (Te), % 0
0 to 0.00020