MakeItFrom.com
Menu (ESC)

AWS E410 vs. CR014A Copper

AWS E410 belongs to the iron alloys classification, while CR014A copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS E410 and the bottom bar is CR014A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 23
15
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
43
Tensile Strength: Ultimate (UTS), MPa 580
230
Tensile Strength: Yield (Proof), MPa 440
140

Thermal Properties

Latent Heat of Fusion, J/g 270
210
Melting Completion (Liquidus), °C 1450
1090
Melting Onset (Solidus), °C 1400
1040
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 28
380
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
98
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
99

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
32
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 2.0
2.6
Embodied Energy, MJ/kg 28
42
Embodied Water, L/kg 100
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
31
Resilience: Unit (Modulus of Resilience), kJ/m3 500
83
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21
7.1
Strength to Weight: Bending, points 20
9.3
Thermal Diffusivity, mm2/s 7.5
110
Thermal Shock Resistance, points 16
8.1

Alloy Composition

Bismuth (Bi), % 0
0 to 0.00050
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 11 to 13.5
0
Copper (Cu), % 0 to 0.75
99.913 to 99.969
Iron (Fe), % 82.2 to 89
0
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 0 to 0.7
0
Phosphorus (P), % 0 to 0.040
0.0010 to 0.0070
Silicon (Si), % 0 to 0.9
0
Silver (Ag), % 0
0.030 to 0.050
Sulfur (S), % 0 to 0.030
0