AWS E410 vs. C37100 Brass

AWS E410 belongs to the iron alloys classification, while C37100 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E410 and the bottom bar is C37100 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
100
Elongation at Break, % 23
8.0 to 40
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 76
40
Tensile Strength: Ultimate (UTS), MPa 580
370 to 520
Tensile Strength: Yield (Proof), MPa 440
150 to 390

Thermal Properties

Latent Heat of Fusion, J/g 270
170
Melting Completion (Liquidus), °C 1450
900
Melting Onset (Solidus), °C 1400
890
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 28
120
Thermal Expansion, µm/m-K 14
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
27
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
30

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
23
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 2.0
2.7
Embodied Energy, MJ/kg 28
45
Embodied Water, L/kg 100
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
38 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 500
110 to 750
Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 21
13 to 18
Strength to Weight: Bending, points 20
14 to 18
Thermal Diffusivity, mm2/s 7.5
39
Thermal Shock Resistance, points 16
12 to 17

Alloy Composition

Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 11 to 13.5
0
Copper (Cu), % 0 to 0.75
58 to 62
Iron (Fe), % 82.2 to 89
0 to 0.15
Lead (Pb), % 0
0.6 to 1.2
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 0 to 0.7
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 0.9
0
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
36.3 to 41.4
Residuals, % 0
0 to 0.4