AWS E410 vs. ZA-12

AWS E410 belongs to the iron alloys classification, while ZA-12 belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E410 and the bottom bar is ZA-12.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
83
Elongation at Break, % 23
1.6 to 5.3
Poisson's Ratio 0.28
0.26
Shear Modulus, GPa 76
33
Tensile Strength: Ultimate (UTS), MPa 580
260 to 400
Tensile Strength: Yield (Proof), MPa 440
210 to 320

Thermal Properties

Latent Heat of Fusion, J/g 270
120
Melting Completion (Liquidus), °C 1450
430
Melting Onset (Solidus), °C 1400
380
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 28
120
Thermal Expansion, µm/m-K 14
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
28
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
42

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
11
Density, g/cm3 7.8
6.0
Embodied Carbon, kg CO2/kg material 2.0
3.4
Embodied Energy, MJ/kg 28
64
Embodied Water, L/kg 100
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
4.0 to 20
Resilience: Unit (Modulus of Resilience), kJ/m3 500
260 to 620
Stiffness to Weight: Axial, points 14
7.6
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
12 to 19
Strength to Weight: Bending, points 20
15 to 20
Thermal Diffusivity, mm2/s 7.5
43
Thermal Shock Resistance, points 16
9.4 to 14

Alloy Composition

Aluminum (Al), % 0
10.5 to 11.5
Cadmium (Cd), % 0
0 to 0.0060
Carbon (C), % 0 to 0.12
0
Chromium (Cr), % 11 to 13.5
0
Copper (Cu), % 0 to 0.75
0.5 to 1.2
Iron (Fe), % 82.2 to 89
0 to 0.075
Lead (Pb), % 0
0 to 0.0060
Magnesium (Mg), % 0
0.015 to 0.030
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 0 to 0.7
0 to 0.020
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 0.9
0 to 0.060
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.0030
Zinc (Zn), % 0
87.1 to 89