MakeItFrom.com
Menu (ESC)

AWS E410NiMo vs. AWS E2209

Both AWS E410NiMo and AWS E2209 are iron alloys. They have 81% of their average alloy composition in common.

For each property being compared, the top bar is AWS E410NiMo and the bottom bar is AWS E2209.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
23
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 850
770

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 24
16
Thermal Expansion, µm/m-K 14
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 10
20
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.4
4.0
Embodied Energy, MJ/kg 34
55
Embodied Water, L/kg 110
170

Common Calculations

PREN (Pitting Resistance) 14
35
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
27
Strength to Weight: Bending, points 26
24
Thermal Diffusivity, mm2/s 6.5
4.3
Thermal Shock Resistance, points 23
20

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.040
Chromium (Cr), % 11 to 12.5
21.5 to 23.5
Copper (Cu), % 0 to 0.75
0 to 0.75
Iron (Fe), % 79 to 84.6
58.4 to 66.9
Manganese (Mn), % 0 to 1.0
0.5 to 2.0
Molybdenum (Mo), % 0.4 to 0.7
2.5 to 3.5
Nickel (Ni), % 4.0 to 5.0
8.5 to 10.5
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030