AWS E410NiMo vs. EN 1.1233 Steel

Both AWS E410NiMo and EN 1.1233 steel are iron alloys. They have 83% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E410NiMo and the bottom bar is EN 1.1233 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 850
680 to 760

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 24
51
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 10
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.4
1.4
Embodied Energy, MJ/kg 34
19
Embodied Water, L/kg 110
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
24 to 27
Strength to Weight: Bending, points 26
22 to 24
Thermal Diffusivity, mm2/s 6.5
14
Thermal Shock Resistance, points 23
22 to 24

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.060
0.52 to 0.6
Chromium (Cr), % 11 to 12.5
0
Copper (Cu), % 0 to 0.75
0 to 0.3
Iron (Fe), % 79 to 84.6
98 to 99.1
Manganese (Mn), % 0 to 1.0
0.9 to 1.2
Molybdenum (Mo), % 0.4 to 0.7
0
Nickel (Ni), % 4.0 to 5.0
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.9
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030