AWS E410NiMo vs. EN 1.4313 Stainless Steel
Both AWS E410NiMo and EN 1.4313 stainless steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS E410NiMo and the bottom bar is EN 1.4313 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 17 | |
| 12 to 17 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 750 to 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 280 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1450 |
| Melting Onset (Solidus), °C | 1400 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 24 | |
| 25 |
| Thermal Expansion, µm/m-K | 14 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.7 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.1 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 10 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 2.4 |
| Embodied Energy, MJ/kg | 34 | |
| 34 |
| Embodied Water, L/kg | 110 | |
| 110 |
Common Calculations
| PREN (Pitting Resistance) | 14 | |
| 15 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 30 | |
| 27 to 36 |
| Strength to Weight: Bending, points | 26 | |
| 23 to 28 |
| Thermal Diffusivity, mm2/s | 6.5 | |
| 6.7 |
| Thermal Shock Resistance, points | 23 | |
| 27 to 36 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0 to 0.050 |
| Chromium (Cr), % | 11 to 12.5 | |
| 12 to 14 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Iron (Fe), % | 79 to 84.6 | |
| 78.5 to 84.2 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0.4 to 0.7 | |
| 0.3 to 0.7 |
| Nickel (Ni), % | 4.0 to 5.0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.9 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |