AWS E410NiMo vs. S39277 Stainless Steel

Both AWS E410NiMo and S39277 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E410NiMo and the bottom bar is S39277 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
28
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 850
930

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 24
16
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 3.1
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 10
23
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.4
4.2
Embodied Energy, MJ/kg 34
59
Embodied Water, L/kg 110
180

Common Calculations

PREN (Pitting Resistance) 14
43
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
33
Strength to Weight: Bending, points 26
27
Thermal Diffusivity, mm2/s 6.5
4.2
Thermal Shock Resistance, points 23
26

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.025
Chromium (Cr), % 11 to 12.5
24 to 26
Copper (Cu), % 0 to 0.75
1.2 to 2.0
Iron (Fe), % 79 to 84.6
56.8 to 64.3
Manganese (Mn), % 0 to 1.0
0 to 0.8
Molybdenum (Mo), % 0.4 to 0.7
3.0 to 4.0
Nickel (Ni), % 4.0 to 5.0
6.5 to 8.0
Nitrogen (N), % 0
0.23 to 0.33
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.9
0 to 0.8
Sulfur (S), % 0 to 0.030
0 to 0.0020
Tungsten (W), % 0
0.8 to 1.2