AWS E70C-Ni2 vs. EN 1.4542 Stainless Steel
Both AWS E70C-Ni2 and EN 1.4542 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS E70C-Ni2 and the bottom bar is EN 1.4542 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 27 | |
| 5.7 to 20 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 560 | |
| 880 to 1470 |
| Tensile Strength: Yield (Proof), MPa | 450 | |
| 580 to 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1430 |
| Melting Onset (Solidus), °C | 1410 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.3 | |
| 13 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 22 | |
| 39 |
| Embodied Water, L/kg | 51 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 62 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 540 | |
| 880 to 4360 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 31 to 52 |
| Strength to Weight: Bending, points | 19 | |
| 26 to 37 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.3 |
| Thermal Shock Resistance, points | 17 | |
| 29 to 49 |
Alloy Composition
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.070 |
| Chromium (Cr), % | 0 | |
| 15 to 17 |
| Copper (Cu), % | 0 to 0.35 | |
| 3.0 to 5.0 |
| Iron (Fe), % | 94.1 to 98.3 | |
| 69.6 to 79 |
| Manganese (Mn), % | 0 to 1.3 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.6 |
| Nickel (Ni), % | 1.8 to 2.8 | |
| 3.0 to 5.0 |
| Niobium (Nb), % | 0 | |
| 0 to 0.45 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.9 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |