AWS E80C-B2 vs. EN 1.4606 Stainless Steel
Both AWS E80C-B2 and EN 1.4606 stainless steel are iron alloys. They have 57% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-B2 and the bottom bar is EN 1.4606 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 22 | |
| 23 to 39 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 600 to 1020 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 280 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 300 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 14 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 2.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.0 | |
| 26 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 6.0 |
| Embodied Energy, MJ/kg | 22 | |
| 87 |
| Embodied Water, L/kg | 53 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 3.0 | |
| 19 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 190 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 740 | |
| 200 to 1010 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 21 to 36 |
| Strength to Weight: Bending, points | 21 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 11 | |
| 3.7 |
| Thermal Shock Resistance, points | 18 | |
| 21 to 35 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.35 |
| Boron (B), % | 0 | |
| 0.0010 to 0.010 |
| Carbon (C), % | 0.050 to 0.12 | |
| 0 to 0.080 |
| Chromium (Cr), % | 1.0 to 1.5 | |
| 13 to 16 |
| Iron (Fe), % | 95.3 to 97.9 | |
| 49.2 to 59 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 0.4 to 0.65 | |
| 1.0 to 1.5 |
| Nickel (Ni), % | 0 to 0.2 | |
| 24 to 27 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.25 to 0.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 1.9 to 2.3 |
| Vanadium (V), % | 0 to 0.030 | |
| 0.1 to 0.5 |
| Residuals, % | 0 to 0.5 | |
| 0 |