AWS E80C-B6 vs. N10629 Nickel
AWS E80C-B6 belongs to the iron alloys classification, while N10629 nickel belongs to the nickel alloys. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-B6 and the bottom bar is N10629 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 19 | |
| 45 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 74 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 310 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1610 |
| Melting Onset (Solidus), °C | 1410 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.7 | |
| 75 |
| Density, g/cm3 | 7.8 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 15 |
| Embodied Energy, MJ/kg | 25 | |
| 190 |
| Embodied Water, L/kg | 71 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 730 | |
| 360 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 22 | |
| 26 |
| Strength to Weight: Bending, points | 21 | |
| 22 |
| Thermal Shock Resistance, points | 18 | |
| 27 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.1 to 0.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.010 |
| Chromium (Cr), % | 4.5 to 6.0 | |
| 0.5 to 1.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 to 0.5 |
| Iron (Fe), % | 90.1 to 94.4 | |
| 1.0 to 6.0 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0.45 to 0.65 | |
| 26 to 30 |
| Nickel (Ni), % | 0 to 0.6 | |
| 65 to 72.4 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.25 to 0.6 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |