AWS E80C-B8 vs. 201.0 Aluminum

AWS E80C-B8 belongs to the iron alloys classification, while 201.0 aluminum belongs to the aluminum alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS E80C-B8 and the bottom bar is 201.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
71
Elongation at Break, % 19
4.4 to 20
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 75
27
Tensile Strength: Ultimate (UTS), MPa 620
370 to 470
Tensile Strength: Yield (Proof), MPa 540
220 to 400

Thermal Properties

Latent Heat of Fusion, J/g 270
390
Melting Completion (Liquidus), °C 1450
650
Melting Onset (Solidus), °C 1410
570
Specific Heat Capacity, J/kg-K 470
870
Thermal Conductivity, W/m-K 25
120
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.1
30 to 33
Electrical Conductivity: Equal Weight (Specific), % IACS 11
87 to 97

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
38
Density, g/cm3 7.8
3.1
Embodied Carbon, kg CO2/kg material 2.1
8.7
Embodied Energy, MJ/kg 28
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
19 to 63
Resilience: Unit (Modulus of Resilience), kJ/m3 740
330 to 1160
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
45
Strength to Weight: Axial, points 22
33 to 42
Strength to Weight: Bending, points 21
37 to 44
Thermal Diffusivity, mm2/s 6.9
45
Thermal Shock Resistance, points 17
19 to 25

Alloy Composition

Aluminum (Al), % 0
92.1 to 95.1
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 8.0 to 10.5
0
Copper (Cu), % 0 to 0.35
4.0 to 5.2
Iron (Fe), % 85.5 to 90.6
0 to 0.15
Magnesium (Mg), % 0
0.15 to 0.55
Manganese (Mn), % 0.4 to 1.0
0.2 to 0.5
Molybdenum (Mo), % 0.8 to 1.2
0
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.25 to 0.6
0 to 0.1
Silver (Ag), % 0
0.4 to 1.0
Sulfur (S), % 0 to 0.025
0
Titanium (Ti), % 0
0.15 to 0.35
Vanadium (V), % 0 to 0.030
0
Residuals, % 0
0 to 0.1