MakeItFrom.com
Menu (ESC)

AWS E80C-B8 vs. EN 1.0114 Steel

Both AWS E80C-B8 and EN 1.0114 steel are iron alloys. They have 89% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B8 and the bottom bar is EN 1.0114 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
25
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 620
430
Tensile Strength: Yield (Proof), MPa 540
220

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 11
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
1.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.1
1.4
Embodied Energy, MJ/kg 28
18
Embodied Water, L/kg 89
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
88
Resilience: Unit (Modulus of Resilience), kJ/m3 740
130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
15
Strength to Weight: Bending, points 21
16
Thermal Diffusivity, mm2/s 6.9
14
Thermal Shock Resistance, points 17
13

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.19
Chromium (Cr), % 8.0 to 10.5
0
Copper (Cu), % 0 to 0.35
0 to 0.6
Iron (Fe), % 85.5 to 90.6
97.6 to 100
Manganese (Mn), % 0.4 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.8 to 1.2
0
Nickel (Ni), % 0 to 0.2
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.25 to 0.6
0
Sulfur (S), % 0 to 0.025
0 to 0.040
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0