AWS E80C-B8 vs. EN 1.4446 Stainless Steel

Both AWS E80C-B8 and EN 1.4446 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B8 and the bottom bar is EN 1.4446 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
23
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 75
79
Tensile Strength: Ultimate (UTS), MPa 620
490
Tensile Strength: Yield (Proof), MPa 540
240

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 11
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.1
4.5
Embodied Energy, MJ/kg 28
60
Embodied Water, L/kg 89
160

Common Calculations

PREN (Pitting Resistance) 13
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
93
Resilience: Unit (Modulus of Resilience), kJ/m3 740
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 21
17
Thermal Diffusivity, mm2/s 6.9
3.6
Thermal Shock Resistance, points 17
11

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.030
Chromium (Cr), % 8.0 to 10.5
16.5 to 18.5
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 85.5 to 90.6
59.7 to 66.9
Manganese (Mn), % 0.4 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.8 to 1.2
4.0 to 4.5
Nickel (Ni), % 0 to 0.2
12.5 to 14.5
Nitrogen (N), % 0
0.12 to 0.22
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.25 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0