AWS E80C-B8 vs. Grade CX2MW Nickel

AWS E80C-B8 belongs to the iron alloys classification, while grade CX2MW nickel belongs to the nickel alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B8 and the bottom bar is grade CX2MW nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 19
34
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
84
Tensile Strength: Ultimate (UTS), MPa 620
620
Tensile Strength: Yield (Proof), MPa 540
350

Thermal Properties

Latent Heat of Fusion, J/g 270
330
Melting Completion (Liquidus), °C 1450
1550
Melting Onset (Solidus), °C 1410
1490
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 25
10
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.1
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 11
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
65
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 2.1
12
Embodied Energy, MJ/kg 28
170
Embodied Water, L/kg 89
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
180
Resilience: Unit (Modulus of Resilience), kJ/m3 740
290
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 21
18
Thermal Diffusivity, mm2/s 6.9
2.7
Thermal Shock Resistance, points 17
17

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.020
Chromium (Cr), % 8.0 to 10.5
20 to 22.5
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 85.5 to 90.6
2.0 to 6.0
Manganese (Mn), % 0.4 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.8 to 1.2
12.5 to 14.5
Nickel (Ni), % 0 to 0.2
51.3 to 63
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.25 to 0.6
0 to 0.8
Sulfur (S), % 0 to 0.025
0 to 0.025
Tungsten (W), % 0
2.5 to 3.5
Vanadium (V), % 0 to 0.030
0 to 0.35
Residuals, % 0 to 0.5
0