AWS E80C-B8 vs. SAE-AISI 1019 Steel
Both AWS E80C-B8 and SAE-AISI 1019 steel are iron alloys. They have 89% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-B8 and the bottom bar is SAE-AISI 1019 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 19 | |
| 17 to 29 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 470 to 520 |
| Tensile Strength: Yield (Proof), MPa | 540 | |
| 250 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 25 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.1 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 28 | |
| 18 |
| Embodied Water, L/kg | 89 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 82 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 740 | |
| 160 to 500 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 17 to 18 |
| Strength to Weight: Bending, points | 21 | |
| 17 to 18 |
| Thermal Diffusivity, mm2/s | 6.9 | |
| 14 |
| Thermal Shock Resistance, points | 17 | |
| 15 to 16 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.15 to 0.2 |
| Chromium (Cr), % | 8.0 to 10.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 |
| Iron (Fe), % | 85.5 to 90.6 | |
| 98.7 to 99.15 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 0.8 to 1.2 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.25 to 0.6 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.050 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |