AWS E80C-B8 vs. S28200 Stainless Steel
Both AWS E80C-B8 and S28200 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-B8 and the bottom bar is S28200 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 19 | |
| 45 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 870 |
| Tensile Strength: Yield (Proof), MPa | 540 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 290 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1380 |
| Melting Onset (Solidus), °C | 1410 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 12 |
| Density, g/cm3 | 7.8 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 2.1 | |
| 2.8 |
| Embodied Energy, MJ/kg | 28 | |
| 41 |
| Embodied Water, L/kg | 89 | |
| 160 |
Common Calculations
| PREN (Pitting Resistance) | 13 | |
| 29 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 330 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 740 | |
| 540 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 25 | |
| 26 |
| Strength to Weight: Axial, points | 22 | |
| 32 |
| Strength to Weight: Bending, points | 21 | |
| 27 |
| Thermal Shock Resistance, points | 17 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.15 |
| Chromium (Cr), % | 8.0 to 10.5 | |
| 17 to 19 |
| Copper (Cu), % | 0 to 0.35 | |
| 0.75 to 1.3 |
| Iron (Fe), % | 85.5 to 90.6 | |
| 57.7 to 64.1 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 17 to 19 |
| Molybdenum (Mo), % | 0.8 to 1.2 | |
| 0.75 to 1.3 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.4 to 0.6 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.25 to 0.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |