AWS E80C-B8 vs. Z40101 Zinc

AWS E80C-B8 belongs to the iron alloys classification, while Z40101 zinc belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-B8 and the bottom bar is Z40101 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 19
44
Poisson's Ratio 0.28
0.25
Shear Modulus, GPa 75
35
Tensile Strength: Ultimate (UTS), MPa 620
130
Tensile Strength: Yield (Proof), MPa 540
110

Thermal Properties

Latent Heat of Fusion, J/g 270
110
Melting Completion (Liquidus), °C 1450
410
Melting Onset (Solidus), °C 1410
400
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 25
110
Thermal Expansion, µm/m-K 13
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.1
27
Electrical Conductivity: Equal Weight (Specific), % IACS 11
37

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
11
Density, g/cm3 7.8
6.6
Embodied Carbon, kg CO2/kg material 2.1
2.8
Embodied Energy, MJ/kg 28
53
Embodied Water, L/kg 89
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
56
Resilience: Unit (Modulus of Resilience), kJ/m3 740
69
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 22
5.7
Strength to Weight: Bending, points 21
8.9
Thermal Diffusivity, mm2/s 6.9
44
Thermal Shock Resistance, points 17
4.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 8.0 to 10.5
0
Copper (Cu), % 0 to 0.35
0.080 to 0.4
Iron (Fe), % 85.5 to 90.6
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Manganese (Mn), % 0.4 to 1.0
0
Molybdenum (Mo), % 0.8 to 1.2
0
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0.25 to 0.6
0
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0 to 0.020
Vanadium (V), % 0 to 0.030
0
Zinc (Zn), % 0
99.542 to 99.92
Residuals, % 0 to 0.5
0