AWS E80C-W2 vs. EN 1.7230 Steel
Both AWS E80C-W2 and EN 1.7230 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-W2 and the bottom bar is EN 1.7230 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 25 | |
| 11 to 12 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 720 to 910 |
| Tensile Strength: Yield (Proof), MPa | 540 | |
| 510 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 44 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 2.4 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.5 |
| Embodied Energy, MJ/kg | 20 | |
| 20 |
| Embodied Water, L/kg | 51 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 79 to 97 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 770 | |
| 700 to 1460 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 26 to 32 |
| Strength to Weight: Bending, points | 21 | |
| 23 to 27 |
| Thermal Diffusivity, mm2/s | 10 | |
| 12 |
| Thermal Shock Resistance, points | 18 | |
| 21 to 27 |
Alloy Composition
| Carbon (C), % | 0 to 0.12 | |
| 0.3 to 0.37 |
| Chromium (Cr), % | 0.45 to 0.7 | |
| 0.8 to 1.2 |
| Copper (Cu), % | 0.3 to 0.75 | |
| 0 |
| Iron (Fe), % | 94.9 to 98 | |
| 96.7 to 98.3 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.3 |
| Nickel (Ni), % | 0.4 to 0.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.35 to 0.8 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |