AWS E80C-W2 vs. CC763S Brass
AWS E80C-W2 belongs to the iron alloys classification, while CC763S brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AWS E80C-W2 and the bottom bar is CC763S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 25 | |
| 7.3 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 72 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 540 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 190 |
| Melting Completion (Liquidus), °C | 1450 | |
| 870 |
| Melting Onset (Solidus), °C | 1410 | |
| 830 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Expansion, µm/m-K | 13 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 29 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 32 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 24 |
| Density, g/cm3 | 7.8 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.9 |
| Embodied Energy, MJ/kg | 20 | |
| 49 |
| Embodied Water, L/kg | 51 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 30 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 770 | |
| 340 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 22 | |
| 17 |
| Strength to Weight: Bending, points | 21 | |
| 17 |
| Thermal Shock Resistance, points | 18 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 1.0 to 2.5 |
| Antimony (Sb), % | 0 | |
| 0 to 0.080 |
| Carbon (C), % | 0 to 0.12 | |
| 0 |
| Chromium (Cr), % | 0.45 to 0.7 | |
| 0 |
| Copper (Cu), % | 0.3 to 0.75 | |
| 56.5 to 67 |
| Iron (Fe), % | 94.9 to 98 | |
| 0.5 to 2.0 |
| Lead (Pb), % | 0 | |
| 0 to 1.5 |
| Manganese (Mn), % | 0.5 to 1.3 | |
| 1.0 to 3.5 |
| Nickel (Ni), % | 0.4 to 0.8 | |
| 0 to 2.5 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.35 to 0.8 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 1.0 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 18.9 to 41 |
| Residuals, % | 0 to 0.5 | |
| 0 |