AWS E90C-B9 vs. R04295 Alloy
AWS E90C-B9 belongs to the iron alloys classification, while R04295 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS E90C-B9 and the bottom bar is R04295 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
100 |
Elongation at Break, % | 18 | |
22 |
Poisson's Ratio | 0.28 | |
0.38 |
Shear Modulus, GPa | 75 | |
37 |
Tensile Strength: Ultimate (UTS), MPa | 710 | |
410 |
Tensile Strength: Yield (Proof), MPa | 460 | |
300 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
300 |
Specific Heat Capacity, J/kg-K | 470 | |
260 |
Thermal Expansion, µm/m-K | 13 | |
7.2 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.8 | |
9.0 |
Embodied Water, L/kg | 91 | |
950 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
84 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
430 |
Stiffness to Weight: Axial, points | 14 | |
6.3 |
Stiffness to Weight: Bending, points | 25 | |
17 |
Strength to Weight: Axial, points | 25 | |
13 |
Strength to Weight: Bending, points | 23 | |
14 |
Thermal Shock Resistance, points | 20 | |
40 |
Alloy Composition
Aluminum (Al), % | 0 to 0.040 | |
0 |
Carbon (C), % | 0.080 to 0.13 | |
0 to 0.015 |
Chromium (Cr), % | 8.0 to 10.5 | |
0 |
Copper (Cu), % | 0 to 0.2 | |
0 |
Hafnium (Hf), % | 0 | |
9.0 to 11 |
Hydrogen (H), % | 0 | |
0 to 0.0015 |
Iron (Fe), % | 84.4 to 90.9 | |
0 |
Manganese (Mn), % | 0 to 1.2 | |
0 |
Molybdenum (Mo), % | 0.85 to 1.2 | |
0 |
Nickel (Ni), % | 0 to 0.8 | |
0 |
Niobium (Nb), % | 0.020 to 0.1 | |
85.9 to 90.3 |
Nitrogen (N), % | 0.030 to 0.070 | |
0 to 0.010 |
Oxygen (O), % | 0 | |
0 to 0.025 |
Phosphorus (P), % | 0 to 0.020 | |
0 |
Silicon (Si), % | 0 to 0.5 | |
0 |
Sulfur (S), % | 0 to 0.015 | |
0 |
Tantalum (Ta), % | 0 | |
0 to 0.5 |
Titanium (Ti), % | 0 | |
0.7 to 1.3 |
Tungsten (W), % | 0 | |
0 to 0.5 |
Vanadium (V), % | 0.15 to 0.3 | |
0 |
Zirconium (Zr), % | 0 | |
0 to 0.7 |
Residuals, % | 0 to 0.5 | |
0 |