AWS E90C-D2 vs. S30435 Stainless Steel

Both AWS E90C-D2 and S30435 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E90C-D2 and the bottom bar is S30435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
51
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 690
510
Tensile Strength: Yield (Proof), MPa 620
170

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
16
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
14
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
2.9
Embodied Energy, MJ/kg 21
40
Embodied Water, L/kg 49
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
210
Resilience: Unit (Modulus of Resilience), kJ/m3 1010
77
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 13
4.2
Thermal Shock Resistance, points 20
12

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.080
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.35
1.5 to 3.0
Iron (Fe), % 95.5 to 98.6
66.9 to 75.5
Manganese (Mn), % 1.0 to 1.9
0 to 2.0
Molybdenum (Mo), % 0.4 to 0.6
0
Nickel (Ni), % 0
7.0 to 9.0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0