AWS E90C-K3 vs. S40910 Stainless Steel

Both AWS E90C-K3 and S40910 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E90C-K3 and the bottom bar is S40910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 55
23
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 710
430
Tensile Strength: Yield (Proof), MPa 600
190

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
26
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.9
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 9.0
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
2.0
Embodied Energy, MJ/kg 23
28
Embodied Water, L/kg 53
94

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 370
80
Resilience: Unit (Modulus of Resilience), kJ/m3 980
94
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25
16
Strength to Weight: Bending, points 22
16
Thermal Diffusivity, mm2/s 13
6.9
Thermal Shock Resistance, points 21
16

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 0 to 0.15
10.5 to 11.7
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 92.6 to 98.5
85 to 89.5
Manganese (Mn), % 0.75 to 2.3
0 to 1.0
Molybdenum (Mo), % 0.25 to 0.65
0
Nickel (Ni), % 0.5 to 2.5
0 to 0.5
Niobium (Nb), % 0
0 to 0.17
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.020
Titanium (Ti), % 0
0 to 0.5
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0