AWS ENiCrCoMo-1 vs. C43500 Brass
AWS ENiCrCoMo-1 belongs to the nickel alloys classification, while C43500 brass belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS ENiCrCoMo-1 and the bottom bar is C43500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 28 | |
| 8.5 to 46 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 82 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 320 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 190 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1000 |
| Melting Onset (Solidus), °C | 1380 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 380 |
| Thermal Expansion, µm/m-K | 13 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 28 |
| Density, g/cm3 | 8.5 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 2.7 |
| Embodied Energy, MJ/kg | 140 | |
| 45 |
| Embodied Water, L/kg | 340 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 19 |
| Strength to Weight: Axial, points | 23 | |
| 10 to 17 |
| Strength to Weight: Bending, points | 21 | |
| 12 to 17 |
| Thermal Shock Resistance, points | 19 | |
| 11 to 18 |
Alloy Composition
| Carbon (C), % | 0.050 to 0.15 | |
| 0 |
| Chromium (Cr), % | 21 to 26 | |
| 0 |
| Cobalt (Co), % | 9.0 to 15 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 79 to 83 |
| Iron (Fe), % | 0 to 5.0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 | |
| 0 to 0.090 |
| Manganese (Mn), % | 0.3 to 2.5 | |
| 0 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 0 |
| Nickel (Ni), % | 38.6 to 61.7 | |
| 0 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.6 to 1.2 |
| Zinc (Zn), % | 0 | |
| 15.4 to 20.4 |
| Residuals, % | 0 | |
| 0 to 0.3 |