AWS ENiCrMo-10 vs. AWS BAg-1a

AWS ENiCrMo-10 belongs to the nickel alloys classification, while AWS BAg-1a belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ENiCrMo-10 and the bottom bar is AWS BAg-1a.

AWS ENiCrMo-10 (W86022) Weld Metal AWS BAg-1a (P07500) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		77

Poisson's Ratio		0.29
Poisson's Ratio		0.33

Shear Modulus, GPa		84
Shear Modulus, GPa		29

Tensile Strength: Ultimate (UTS), MPa		710
Tensile Strength: Ultimate (UTS), MPa		180

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		120

Melting Completion (Liquidus), °C		1550
Melting Completion (Liquidus), °C		640

Melting Onset (Solidus), °C		1490
Melting Onset (Solidus), °C		630

Specific Heat Capacity, J/kg-K		420
Specific Heat Capacity, J/kg-K		280

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		22

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		9.3

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		48

Embodied Energy, MJ/kg		160
Embodied Energy, MJ/kg		760

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		4.6

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		15

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		5.4

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		7.6

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		7.5

Alloy Composition

Cadmium (Cd), %		0
Cadmium (Cd), %		17 to 19

Carbon (C), %		0 to 0.020
Carbon (C), %		0

Chromium (Cr), %		20 to 22.5
Chromium (Cr), %		0

Cobalt (Co), %		0 to 2.5
Cobalt (Co), %		0

Copper (Cu), %		0 to 0.5
Copper (Cu), %		14.5 to 16.5

Iron (Fe), %		2.0 to 6.0
Iron (Fe), %		0

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0

Molybdenum (Mo), %		12.5 to 14.5
Molybdenum (Mo), %		0

Nickel (Ni), %		48.4 to 63
Nickel (Ni), %		0

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.2
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		49 to 51

Sulfur (S), %		0 to 0.015
Sulfur (S), %		0

Tungsten (W), %		2.5 to 3.5
Tungsten (W), %		0

Vanadium (V), %		0 to 0.35
Vanadium (V), %		0

Zinc (Zn), %		0
Zinc (Zn), %		14.5 to 18.5

Residuals, %		0
Residuals, %		0 to 0.15