AWS ENiCrMo-3 vs. S35000 Stainless Steel
AWS ENiCrMo-3 belongs to the nickel alloys classification, while S35000 stainless steel belongs to the iron alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS ENiCrMo-3 and the bottom bar is S35000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 34 | |
| 2.3 to 14 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 79 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 870 | |
| 1300 to 1570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 280 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 16 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.3 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.4 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 80 | |
| 14 |
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 14 | |
| 3.2 |
| Embodied Energy, MJ/kg | 190 | |
| 44 |
| Embodied Water, L/kg | 290 | |
| 130 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 28 | |
| 46 to 56 |
| Strength to Weight: Bending, points | 24 | |
| 34 to 38 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 4.4 |
| Thermal Shock Resistance, points | 25 | |
| 42 to 51 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.070 to 0.11 |
| Chromium (Cr), % | 20 to 23 | |
| 16 to 17 |
| Cobalt (Co), % | 0 to 0.12 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 7.0 | |
| 72.7 to 76.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.5 to 1.3 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 2.5 to 3.2 |
| Nickel (Ni), % | 55 to 68.9 | |
| 4.0 to 5.0 |
| Niobium (Nb), % | 3.2 to 4.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.070 to 0.13 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |