AWS ENiCrMo-4 vs. EN 1.4029 Stainless Steel

AWS ENiCrMo-4 belongs to the nickel alloys classification, while EN 1.4029 stainless steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS ENiCrMo-4 and the bottom bar is EN 1.4029 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 28
10 to 20
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 84
76
Tensile Strength: Ultimate (UTS), MPa 790
700 to 930

Thermal Properties

Latent Heat of Fusion, J/g 320
270
Melting Completion (Liquidus), °C 1590
1440
Melting Onset (Solidus), °C 1530
1400
Specific Heat Capacity, J/kg-K 410
480
Thermal Expansion, µm/m-K 12
10

Otherwise Unclassified Properties

Base Metal Price, % relative 70
7.0
Density, g/cm3 9.0
7.7
Embodied Carbon, kg CO2/kg material 13
2.0
Embodied Energy, MJ/kg 170
28
Embodied Water, L/kg 280
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 22
25
Strength to Weight: Axial, points 24
25 to 33
Strength to Weight: Bending, points 21
23 to 27
Thermal Shock Resistance, points 22
26 to 34

Alloy Composition

Carbon (C), % 0 to 0.020
0.25 to 0.32
Chromium (Cr), % 14.5 to 16.5
12 to 13.5
Cobalt (Co), % 0 to 2.5
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 4.0 to 7.0
82.8 to 87.6
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 15 to 17
0 to 0.6
Nickel (Ni), % 49.9 to 63.5
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.2
0 to 1.0
Sulfur (S), % 0 to 0.030
0.15 to 0.25
Tungsten (W), % 3.0 to 4.5
0
Vanadium (V), % 0 to 0.35
0
Residuals, % 0 to 0.5
0