AWS ENiCrMo-4 vs. R30075 Cobalt
AWS ENiCrMo-4 belongs to the nickel alloys classification, while R30075 cobalt belongs to the cobalt alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ENiCrMo-4 and the bottom bar is R30075 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 210 to 250 |
| Elongation at Break, % | 28 | |
| 12 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 84 | |
| 82 to 98 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 780 to 1280 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 320 |
| Melting Completion (Liquidus), °C | 1590 | |
| 1360 |
| Melting Onset (Solidus), °C | 1530 | |
| 1290 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.0 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 8.1 |
| Embodied Energy, MJ/kg | 170 | |
| 110 |
| Embodied Water, L/kg | 280 | |
| 530 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 to 17 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 24 | |
| 26 to 42 |
| Strength to Weight: Bending, points | 21 | |
| 22 to 31 |
| Thermal Shock Resistance, points | 22 | |
| 21 to 29 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.1 |
| Boron (B), % | 0 | |
| 0 to 0.010 |
| Carbon (C), % | 0 to 0.020 | |
| 0 to 0.35 |
| Chromium (Cr), % | 14.5 to 16.5 | |
| 27 to 30 |
| Cobalt (Co), % | 0 to 2.5 | |
| 58.7 to 68 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 4.0 to 7.0 | |
| 0 to 0.75 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 15 to 17 | |
| 5.0 to 7.0 |
| Nickel (Ni), % | 49.9 to 63.5 | |
| 0 to 0.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Tungsten (W), % | 3.0 to 4.5 | |
| 0 to 0.2 |
| Vanadium (V), % | 0 to 0.35 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |