AWS ER110S-1 vs. EN 1.4405 Stainless Steel

Both AWS ER110S-1 and EN 1.4405 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS ER110S-1 and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
17
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 870
860
Tensile Strength: Yield (Proof), MPa 740
610

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 47
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
2.8
Embodied Energy, MJ/kg 25
39
Embodied Water, L/kg 55
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
130
Resilience: Unit (Modulus of Resilience), kJ/m3 1460
950
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 31
31
Strength to Weight: Bending, points 26
26
Thermal Diffusivity, mm2/s 13
4.6
Thermal Shock Resistance, points 26
29

Alloy Composition

Aluminum (Al), % 0 to 0.1
0
Carbon (C), % 0 to 0.090
0 to 0.060
Chromium (Cr), % 0 to 0.5
15 to 17
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 92.8 to 96.3
73.6 to 80.3
Manganese (Mn), % 1.4 to 1.8
0 to 1.0
Molybdenum (Mo), % 0.25 to 0.55
0.7 to 1.5
Nickel (Ni), % 1.9 to 2.6
4.0 to 6.0
Phosphorus (P), % 0 to 0.010
0 to 0.035
Silicon (Si), % 0.2 to 0.55
0 to 0.8
Sulfur (S), % 0 to 0.010
0 to 0.025
Titanium (Ti), % 0 to 0.1
0
Vanadium (V), % 0 to 0.040
0
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0 to 0.5
0