AWS ER110S-1 vs. C97300 Nickel Silver

AWS ER110S-1 belongs to the iron alloys classification, while C97300 nickel silver belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AWS ER110S-1 and the bottom bar is C97300 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 17
9.0
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
40
Tensile Strength: Ultimate (UTS), MPa 870
230
Tensile Strength: Yield (Proof), MPa 740
110

Thermal Properties

Latent Heat of Fusion, J/g 250
180
Melting Completion (Liquidus), °C 1460
1040
Melting Onset (Solidus), °C 1410
1010
Specific Heat Capacity, J/kg-K 470
370
Thermal Conductivity, W/m-K 47
29
Thermal Expansion, µm/m-K 13
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
6.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
30
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.8
3.7
Embodied Energy, MJ/kg 25
59
Embodied Water, L/kg 55
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
18
Resilience: Unit (Modulus of Resilience), kJ/m3 1460
59
Stiffness to Weight: Axial, points 13
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 31
7.6
Strength to Weight: Bending, points 26
9.8
Thermal Diffusivity, mm2/s 13
9.3
Thermal Shock Resistance, points 26
8.0

Alloy Composition

Aluminum (Al), % 0 to 0.1
0 to 0.0050
Antimony (Sb), % 0
0 to 0.35
Carbon (C), % 0 to 0.090
0
Chromium (Cr), % 0 to 0.5
0
Copper (Cu), % 0 to 0.25
53 to 58
Iron (Fe), % 92.8 to 96.3
0 to 1.5
Lead (Pb), % 0
8.0 to 11
Manganese (Mn), % 1.4 to 1.8
0
Molybdenum (Mo), % 0.25 to 0.55
0
Nickel (Ni), % 1.9 to 2.6
11 to 14
Phosphorus (P), % 0 to 0.010
0 to 0.050
Silicon (Si), % 0.2 to 0.55
0 to 0.15
Sulfur (S), % 0 to 0.010
0 to 0.080
Tin (Sn), % 0
1.5 to 3.0
Titanium (Ti), % 0 to 0.1
0
Vanadium (V), % 0 to 0.040
0
Zinc (Zn), % 0
17 to 25
Zirconium (Zr), % 0 to 0.1
0
Residuals, % 0
0 to 1.0