AWS ER70S-B2L vs. EN 1.0452 Steel

Both AWS ER70S-B2L and EN 1.0452 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS ER70S-B2L and the bottom bar is EN 1.0452 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
25
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 590
430
Tensile Strength: Yield (Proof), MPa 450
290

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
48
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
2.1
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
1.5
Embodied Energy, MJ/kg 21
19
Embodied Water, L/kg 54
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
94
Resilience: Unit (Modulus of Resilience), kJ/m3 530
220
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
15
Strength to Weight: Bending, points 20
16
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 17
13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.050
0 to 0.17
Chromium (Cr), % 1.2 to 1.5
0 to 0.3
Copper (Cu), % 0 to 0.35
0 to 0.3
Iron (Fe), % 95.3 to 97.6
97.1 to 99.58
Manganese (Mn), % 0.4 to 0.7
0.4 to 1.2
Molybdenum (Mo), % 0.4 to 0.65
0 to 0.080
Nickel (Ni), % 0 to 0.2
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.4 to 0.7
0 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.010
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020
Residuals, % 0 to 0.5
0