AWS ER70S-B2L vs. EN 1.3543 Stainless Steel

Both AWS ER70S-B2L and EN 1.3543 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ER70S-B2L and the bottom bar is EN 1.3543 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 590
730

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
22
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.3
Embodied Energy, MJ/kg 21
32
Embodied Water, L/kg 54
120

Common Calculations

PREN (Pitting Resistance) 3.1
19
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
27
Strength to Weight: Bending, points 20
24
Thermal Diffusivity, mm2/s 11
6.1
Thermal Shock Resistance, points 17
26

Alloy Composition

Carbon (C), % 0 to 0.050
1.0 to 1.2
Chromium (Cr), % 1.2 to 1.5
16 to 18
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 95.3 to 97.6
79.1 to 83.6
Manganese (Mn), % 0.4 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.4 to 0.65
0.4 to 0.8
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.4 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Residuals, % 0 to 0.5
0