AWS ER80S-B2 vs. ASTM B540 Palladium
AWS ER80S-B2 belongs to the iron alloys classification, while ASTM B540 palladium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ER80S-B2 and the bottom bar is ASTM B540 palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 21 | |
| 1.1 to 14 |
| Poisson's Ratio | 0.29 | |
| 0.38 |
| Shear Modulus, GPa | 73 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 830 to 1240 |
| Tensile Strength: Yield (Proof), MPa | 540 | |
| 620 to 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 140 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1220 |
| Melting Onset (Solidus), °C | 1420 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 240 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 4.9 to 5.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 3.5 to 3.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 13 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 13 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 760 | |
| 1790 to 4660 |
| Stiffness to Weight: Axial, points | 13 | |
| 4.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 12 |
| Strength to Weight: Axial, points | 22 | |
| 18 to 27 |
| Strength to Weight: Bending, points | 21 | |
| 15 to 20 |
| Thermal Shock Resistance, points | 18 | |
| 41 to 61 |
Alloy Composition
| Carbon (C), % | 0.070 to 0.12 | |
| 0 |
| Chromium (Cr), % | 1.2 to 1.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 13.5 to 14.5 |
| Gold (Au), % | 0 | |
| 9.5 to 10.5 |
| Iron (Fe), % | 95.2 to 97.5 | |
| 0 |
| Manganese (Mn), % | 0.4 to 0.7 | |
| 0 |
| Molybdenum (Mo), % | 0.4 to 0.65 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 34 to 36 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 9.5 to 10.5 |
| Silicon (Si), % | 0.4 to 0.7 | |
| 0 |
| Silver (Ag), % | 0 | |
| 29 to 31 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0.8 to 1.2 |
| Residuals, % | 0 | |
| 0 to 0.3 |