AWS ER80S-B3L vs. EN 1.4612 Stainless Steel
Both AWS ER80S-B3L and EN 1.4612 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is EN 1.4612 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 19 | |
11 |
Poisson's Ratio | 0.29 | |
0.28 |
Shear Modulus, GPa | 74 | |
76 |
Tensile Strength: Ultimate (UTS), MPa | 630 | |
1690 to 1850 |
Tensile Strength: Yield (Proof), MPa | 530 | |
1570 to 1730 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
280 |
Melting Completion (Liquidus), °C | 1460 | |
1450 |
Melting Onset (Solidus), °C | 1420 | |
1400 |
Specific Heat Capacity, J/kg-K | 470 | |
480 |
Thermal Expansion, µm/m-K | 13 | |
11 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 4.1 | |
16 |
Density, g/cm3 | 7.8 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 1.8 | |
3.6 |
Embodied Energy, MJ/kg | 23 | |
50 |
Embodied Water, L/kg | 60 | |
140 |
Common Calculations
PREN (Pitting Resistance) | 6.0 | |
19 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
190 to 210 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
25 |
Strength to Weight: Axial, points | 22 | |
60 to 65 |
Strength to Weight: Bending, points | 21 | |
40 to 43 |
Thermal Shock Resistance, points | 18 | |
58 to 63 |
Alloy Composition
Aluminum (Al), % | 0 | |
1.4 to 1.8 |
Carbon (C), % | 0 to 0.050 | |
0 to 0.015 |
Chromium (Cr), % | 2.3 to 2.7 | |
11 to 12.5 |
Copper (Cu), % | 0 to 0.35 | |
0 |
Iron (Fe), % | 93.6 to 96 | |
71.5 to 75.5 |
Manganese (Mn), % | 0.4 to 0.7 | |
0 to 0.1 |
Molybdenum (Mo), % | 0.9 to 1.2 | |
1.8 to 2.3 |
Nickel (Ni), % | 0 to 0.2 | |
10.2 to 11.3 |
Nitrogen (N), % | 0 | |
0 to 0.010 |
Phosphorus (P), % | 0 to 0.025 | |
0 to 0.010 |
Silicon (Si), % | 0.4 to 0.7 | |
0 to 0.1 |
Sulfur (S), % | 0 to 0.025 | |
0 to 0.0050 |
Titanium (Ti), % | 0 | |
0.2 to 0.5 |
Residuals, % | 0 to 0.5 | |
0 |